Interlaced Three-Dimensional Printed Composites and Machines for Fabricating Same

ABSTRACT

A machine for fabricating three-dimensional interlaced composite components including a frame, a deposition surface, a first set of two or more warp heads, a second set of two or more of warp heads, and a weft inserter. An interlaced composite component including a first set of two or more warp filaments parallel to each other and a first set of two or more weft filaments parallel to each other. Warp filaments are interlaced with, and bonded to, weft filaments s. Warp filaments and weft filaments are interlaced in at least two different weave patterns. Warp filaments and weft filaments are continuous, and the weave patterns transition from one pattern to another.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. patent application Ser. No.14/821,502, filed 7 Aug. 2015, which application claims priority to U.S.Provisional Patent Application No. 62/034,930 filed 8 Aug. 2014, theentire contents and substance of each hereby incorporated by reference.

BACKGROUND OF THE INVENTION 1. Field of the Invention

The disclosure relates to the field of composite materials. Morespecifically, the disclosure relates to composites having interlacedfibers in a polymer matrix.

2. Description of Related Art

Polymer composite materials include a matrix material and one or morereinforcing materials. The reinforcing materials enhance the strengthand/or stiffness of the product while the polymer matrix allows thecomposite to be formed in complex shapes. The earliest compositematerials were reinforced with paper or cotton fabric. Later polymercomposites were reinforced by chopped or broken reinforcing fibersrandomly disturbed within the matrix. The discontinuous nature of thereinforcing fibers prevented them from achieving significantreinforcement because the strength between isolated fibers was limitedby the strength of the matrix material itself or by the adhesion betweenthe matrix material and the fibers.

Later polymer composites incorporated woven mats of reinforcing fibers.The woven mats allowed the full strength and stiffness of the fibers tobe employed when the composite was loaded in tension, and to a lesserextent when loaded in compression and flexion. Woven mats also allowedthe strands of the reinforcing fibers to be oriented in the optimaldirection, or a combination of directions, depending on the expectedloading of the part. However, composites manufactured from woven matsgreatly increased manufacturing cost and complexity because the matsgenerally need to be pre-cut and laid in the mold by hand.

Three-dimensional (3D) printing is the process of creating a finishedpart by depositing (adding) layer after layer of material, until thedesired part is obtained. The oldest form of 3D printing isstereolithography, where a bath of liquid polymer is selectivelypolymerized at its surface by UV radiation. The solidified polymer isthen submerged into the liquid so that additional layers can be builtupon the previous layers.

The next major innovation in 3D printing was the development of filamentdeposition modeling (FDM). FDM melts a polymeric or metallic filamentand deposits the molten material in thin layers. FDM is faster thanstereolithography and allows a wider variety of printing materials.However, neither FDM printing or stereolithography is well suited tofabricating structural components. The first 3D printing system suitablefor the fabrication of structural components was selective lasersintering. In this system, a thin layer of metal powder is depositedonto the print surface and selectively sintered by a laser. Anotherlayer of powder is applied over the previously sintered layer, and theprocess is repeated, so that the second layer is sintered to the first.While these sintered metal components fabricated are suitable forstructural applications, their relatively high density makes themunsuitable for some application. Various attempts have been made toadapt FDM printing to create structural composites by addingreinforcement fibers into the polymer filament. While this does improvethe mechanical properties, the strength of the fabricated componentsremains insufficient for use in high-performance applications.

Automated tape placement is a highly precise process for creatingcomposites from unidirectional pre-impregnated textiles (prepreg)textiles. It can be thought of as a more advanced version of the handlay-up FRP processes, where the human operator is replaced by a robot.This permits very precise fiber placement, but it can only be used onrelatively simple curvilinear surfaces. Composites fabricated byautomated tape placement are cured by the same methods as hand lay-up.

SUMMARY OF THE INVENTION

In a first exemplary embodiment of the present invention, a machine forfabricating three-dimensional interlaced composite components isdisclosed, comprising a frame, a deposition surface, a first set of twoor more warp heads adapted to deposit a first set of warp filaments onthe deposition surface in a first warp direction and move parallel toone another within a first plane, a second set of two or more of warpheads adapted to deposit a second set of warp filaments on thedeposition surface in a second warp direction and move parallel to oneanother within the first plane, wherein the second set of warp heads donot move collinearly with the first set of warp heads, and a weftinserter adapted to deposit a set of weft filaments on the depositionsurface in a weft direction and traverse a length of the depositionsurface in the warp direction, wherein the weft direction is differentthan at least one of the first and second warp directions.

One or more of the first set warp heads, the second set warp heads, andthe weft inserter can be supported by the frame. The deposition surfacecan be supported by the frame.

The first warp direction can be the same as the second warp direction.The first warp direction can be different than the second warpdirection. The weft direction can be different than both the first andsecond warp directions.

The weft inserter can comprise a rapier weft inserter comprising alinear element that extends over the deposition surface.

The weft inserter can comprise an air-jet weft inserter comprising acompressed air supply, at least one compressed air control valve, afilament cutter, and a nozzle.

The machine can further comprise a filament cutter.

The deposition surface can be adapted to move linearly in a verticaldirection along a vertical axis. The deposition surface can be adaptedto rotate in a plane normal a vertical axis. The deposition surface canbe adapted to both move linearly in a vertical direction along avertical axis and rotate in a plane normal the vertical axis.

The machine can further comprise a third set of two or more warp headsadapted to deposit warp filaments on the deposition surface in a thirdwarp direction and move parallel to one another and collinearly with thefirst set of warp heads, and a fourth set of two or more warp headsadapted to deposit warp filaments on the deposition surface in a fourthwarp direction, and move parallel to one another collinearly with thesecond set of warp heads.

One or both the third set warp heads and the fourth set warp heads canbe supported by the frame.

In another exemplary embodiment, the present machine can fabricate athree-dimensional interlaced composite by depositing onto the depositionsurface the first set warp filaments, inserting, on top of the first setof warp filaments, a first set of weft filaments, depositing, on top ofthe first set of weft filaments, the second set of warp filaments, andinserting, on top of the second set of warp filaments, a second set ofweft filaments, wherein the three-dimensional interlaced composite isformed when at least one of the warp filaments passes over at least oneof the weft filaments and passes under at least another of the weftfilaments.

In another exemplary embodiment, a three-dimensional interlacedcomposite can be fabricated by the present machine and comprise thefirst set warp filaments and the first set weft filaments.

In another exemplary embodiment, the present invention is an interlacedcomposite component comprising a first set of two or more warp filamentsparallel to each other and a first set of two or more weft filamentsparallel to each other, wherein at least a portion of the warp filamentsof the first set of warp filaments are interlaced with, and bonded to,at least a portion of the weft filaments of the first set of weftfilaments, wherein at least a portion of the warp filaments and at leasta portion of the weft filaments are interlaced in at least two differentweave patterns selected from the group consisting of plain weave, twillweave, and satin weave, and wherein at least a portion of the warpfilaments and at least a portion of the weft filaments are continuousand the weave patterns transition from one pattern to another.

At least a portion of the warp filaments can comprise reinforcing fibersbonded to a polymer matrix. At least a portion of the warp filaments cancomprise reinforcing fibers pre-impregnated with thermoplastic resin. Atleast a portion of the warp filaments and at least a portion of the weftfilaments can comprise comingled reinforcing fibers and thermoplasticfibers.

The interlaced composite component can further comprise a second set oftwo or more warp filaments parallel to each other and a second set oftwo or more weft filaments parallel to each other, wherein at least aportion of the weft filaments of the first set of weft filaments areparallel to one other and substantially coplanar, wherein at least aportion of the weft filaments of the second set weft filaments areparallel to one other, substantially coplanar, and positioned eitherabove or below at least a portion of the first set of weft filaments,wherein at least a portion of the warp filaments of the first set ofwarp filaments alternate between being interlaced with, and bonded to,at least a portion of the weft filaments of the first set of weftfilaments and at least a portion of the weft filaments of the second setof weft filaments, and wherein at least a portion of the warp filamentsof the second set of warp filaments alternate between being interlacedwith, and bonded to, at least a portion of the weft filaments of thefirst set of weft filaments and at least a portion of the weft filamentsof the second set of weft filaments.

At least a portion of the warp filaments of the second set of warpfilaments and at least a portion of the weft filaments of the second setof weft filaments can be interlaced in at least two different weavepatterns selected from the group consisting of plain weave, twill weave,and satin weave, and at least a portion of the warp filaments of thesecond set of warp filaments and at least a portion of the weftfilaments of the second set of weft filaments can be continuous and theweave patterns transition from one pattern to another.

In another exemplary embodiment, the present invention is an interlacedcomposite component comprising a first set of two or more warp filamentsparallel to each other and a first set of two or more weft filamentsparallel to each other, wherein at least a portion of the warp filamentsof the first set of warp filaments are interlaced with, and bonded to,at least a portion of the weft filaments of the first set of weftfilaments, wherein at least a portion of adjacent warp filaments of thefirst set of warp filaments are separated from one another by a warpgap, wherein at least a portion of adjacent weft filaments of the firstset of weft filaments are separated from one another by a weft gap, andwherein the warp and weft gaps define one or more openings in thecomposite component.

The interlaced composite component can further comprise a thermoplasticpolymer, wherein the thermoplastic polymer is molded over the interlacedcomposite component.

The thermoplastic polymer can be reinforced with a discontinuous fiber.

In another exemplary embodiment, a method is described for producing aninterlaced composite. The method includes: depositing onto a depositionsurface a first one or more warp filaments in a first linear direction,inserting, on top of the first one or more warp filaments, a first oneor more weft filaments in a second linear direction, where the seconddirection is in the same plane as the first one or more warp filamentsbut is not parallel to the direction of the first one or more warpfilaments, depositing, on top of the one or more first weft filaments,one or more second warp filaments in first linear direction, where thesecond one or more warp filaments are not collinear with the first oneof more warp filaments, and inserting, on top of the second one or morewarp filaments, a second one or more weft filaments in the seconddirection.

In another exemplary embodiment, a machine for fabricatingthree-dimensional interlaced composite components is disclosed. Themachine includes a frame, a print plate supported by the frame, a firstplurality of warp heads supported by the frame, which deposit filamentson a print plate and move parallel to each other within a first plane.The machine also includes a second plurality of warp heads supported bythe frame which also deposit filaments on the print plate and moveparallel to each other within the first plane and which do not movecoaxially with any of the first plurality of warp heads. The machinealso includes a weft inserter, supported by the frame, which depositsweft filaments on the print plate in a different direction than thefirst and second plurality of warp heads and traverses the length of theprint plate in the same directions as the first and second plurality ofwarp heads.

In another exemplary embodiment, a composite component structure isdisclosed that has a plurality of warp filaments interlaced with, andbonded to, a plurality of weft filaments, where the warp filaments areparallel to each other and include one or more reinforcing fibers bondedto a polymer matrix. The weft filaments are parallel to each other andinclude one or more reinforcing fibers bonded to a polymer matrix. Theplurality of weft filaments and the plurality of weft filaments areinterlaced in at least two of the following weaving patterns: twillweave, and satin weave. The filaments of the plurality of weft filamentsand the filaments of the plurality of weft filaments are continuouswhere the weaving patterns transition from one pattern to another.

These and other objects, features and advantages of the presentinvention will become more apparent upon reading the followingspecification in conjunction with the accompanying drawing figures.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagram of a plain weave illustrating the interlacing ofwarp and weft filaments in accordance with the present disclosure.

FIG. 2 is a diagram of a twill weave illustrating the interlacing ofwarp and weft filaments in accordance with the present disclosure.

FIG. 3 is a diagram of a satin weave illustrating the interlacing ofwarp and weft filaments in accordance with the present disclosure.

FIG. 4 is a sequence of diagrams illustrating the deposition process fora simple 1/1 plain weave in accordance with the present disclosure.

FIG. 5 is a sequence of diagrams illustrating the deposition sequencefor a 2/2 twill weave in accordance with the present disclosure.

FIG. 6 is a sequence of diagrams illustrating the deposition sequencefor a 1/4 satin-weave composite in accordance with the presentdisclosure.

FIG. 7 is a diagram of a composite which integrates three differentweaves within the same interlaced structure, in accordance with thepresent disclosure, to provide different material properties indifferent locations.

FIG. 8 is a diagram of a plain weave where the warp and weft are notorthogonal to each other in accordance with the present disclosure.

FIG. 9 is a schematic illustrating a simplified version of a 3Dinterlaced composite printer in accordance with the present disclosure.

FIG. 10 is a schematic illustrating one embodiment of a warp print head,in accordance with the present disclosure.

FIG. 11 is a schematic illustrating a cross-section of one embodiment ofa warp print head, in accordance with the present disclosure.

FIGS. 12 and 13 are schematics illustrating a more sophisticatedembodiment of a 3D interlaced composite printer in accordance with thepresent disclosure.

FIG. 14 is a schematic illustrating one embodiment of an air-jet weftinsertion system, in accordance with the present disclosure.

FIG. 15 is a schematic illustrating one embodiment of an extendablescissors cutting mechanism, in accordance with the present disclosure.

FIG. 16 is a schematic illustrating one embodiment of a rotary cuttingmechanism, in accordance with the present disclosure.

FIG. 17 is a schematic illustrating one embodiment of a drag knifecutting mechanism, in accordance with the present disclosure.

DETAIL DESCRIPTION OF THE INVENTION

To facilitate an understanding of the principles and features of thevarious embodiments of the invention, various illustrative embodimentsare explained below. Although exemplary embodiments of the invention areexplained in detail, it is to be understood that other embodiments arecontemplated. Accordingly, it is not intended that the invention islimited in its scope to the details of construction and arrangement ofcomponents set forth in the following description or illustrated in thedrawings. The invention is capable of other embodiments and of beingpracticed or carried out in various ways.

As used in the specification and the appended Claims, the singular forms“a,” “an” and “the” include plural references unless the context clearlydictates otherwise. For example, reference to a component is intendedalso to include a composition of a plurality of components. Referencesto a composition containing “a” constituent is intended to include otherconstituents in addition to the one named.

In describing exemplary embodiments, terminology will be resorted to forthe sake of clarity. It is intended that each term contemplates itsbroadest meaning as understood by those skilled in the art and includesall technical equivalents that operate in a similar manner to accomplisha similar purpose.

Ranges may be expressed as from “about” or “approximately” or“substantially” one value and/or to “about” or “approximately” or“substantially” another value. When such a range is expressed, otherexemplary embodiments include from the one value and/or to the othervalue.

Similarly, as used herein, “substantially free” of something, or“substantially pure”, and like characterizations, can include both being“at least substantially free” of something, or “at least substantiallypure”, and being “completely free” of something, or “completely pure”.

“Comprising” or “containing” or “including” is meant that at least thenamed compound, element, particle, or method step is present in thecomposition or article or method, but does not exclude the presence ofother compounds, materials, particles, method steps, even if the othersuch compounds, material, particles, method steps have the same functionas what is named.

The characteristics described as defining the various elements of theinvention are intended to be illustrative and not restrictive. Forexample, if the characteristic is a material, the material includes manysuitable materials that would perform the same or a similar function asthe material(s) described herein are intended to be embraced within thescope of the invention. Such other materials not described herein caninclude, but are not limited to, for example, materials that aredeveloped after the time of the development of the invention.

As used herein, “warp” refers to parallel filaments deposited along theprimary direction of deposition within a plane.

As used herein, “weft” refers to any filaments deposited along any axisnot parallel to the primary direction of deposition within a plane.

As used herein, “plane” refers to the thickness of interlaced compositegenerated during a single pass of the deposition system.

As used herein, “deposition” refers to adding composite filaments to acomposite structure in a controlled fashion and pattern.

As used herein, “composite” refers to a combination of two or morematerials differing in form or composition on a macro scale. As usedherein, a composite includes, at least, a composite matrix binder andreinforcing elements. The composite constituents do not dissolve ormerge completely into one another although they act in concert.

As used herein, “filament” refers to an element including resin andhaving length much greater than its width or diameter. In an exemplaryembodiment, a filament also includes one or more reinforcing fibers.

As used herein, “resin” refers to an isotropic material used as a matrixbinder within a composite.

As used herein, “thermoset” refers to a polymer which solidifies from aliquid form during processing due to an irreversible chemical reaction.

As used herein, “thermoplastic” refers to a polymer which solidifiesfrom a molten form during processing due to freezing.

As used herein, “engineering polymer” refers to polymers having at leastone mechanical, thermal, or electrical material property which issuperior to “bulk” polymers such as polyethylene (PE). Examples ofengineering polymers include, but are not limited to, nylon (PA),polycarbonate (PC), acetal (PMA), polyetheretherketone (PEEK),poly(p-phenylene sulfide)(PPS), and polyetherketoneketone (PEKK).

As used herein, “sizing” refers to pre-coating a reinforcing fiber withanother substance to change its properties during processing.

An FRP composite can be made by laminating layers of unidirectionalfibers. However, a more balanced composite is created by interlacingnon-parallel filaments to create a woven structure. For example, inorthogonal textiles, interlacing the warp and weft yarns generatescrimp, or curvature, in the yarns, which affects the overall mechanicalproperties of the textile. Similar effects are observed in themechanical properties of composites based on interlaced reinforcingfibers. Woven structures can be classified by fabric geometry into thecategories of plain weave, twill weave, and satin weave textiles.

Referring now to the Figures, in which like reference numerals representlike parts, various embodiments of the disclosure will be disclosed indetail. FIG. 1 is an illustration of a plain weave. A plain weave is thesimplest form of textile geometry, comprising a repeat structure wherethe warp fiber passes over one weft yarn and under another weft yarn.Plain weave fabrics have the lowest in-plane stiffness and highestin-plane shear stiffness of any regular fabric geometry, due to thepresence of a high degree of crimp.

FIG. 2 is an illustration of a twill weave. Twill weave fabrics possessa repeat structure where the warp yarn passes over two or three weftyarns before passing under one, two, or three weft yarns. This resultsin the formation of a very characteristic diagonal line. Twill weavespossess moderate in-plane stiffness and shear stiffness.

FIG. 3 is an illustration of a satin weave. The satin weave is the besttextile structure for in-plane stiffness, due to the very low crimpinherent to these weaves. In a satin weave, the warp yarn runs over fouror more weft yarns before interlacing with a weft yarn. While the lowdegree of crimp is good for in-plane stiffness, the lower level ofinterlacing between adjacent yarns translates to low in-plane shearstrength.

Deposition Sequence

The deposition process comprises at least of depositing a continuousfilament in a sequence of short segments of two or more groups of warpfilaments interspersed with depositing intervening weft filaments. In anexemplary embodiment, enough warp filaments are deposited tosubstantially cover the width of the composite component may bedeposited. The length of the warp segments is determined by the desiredpitch of the weft. For clarity and brevity in this section, the warpsegments are referred to as “[numeral] segment, [numeral] [type] group.For example, the first segment of the first group of warp filaments isreferred to as “first segment, first warp group.”

FIG. 4 illustrates the deposition process for a simple 1/1 plain weave.The deposition process begins with deposition of the first segment,first warp group 400. The first weft filament is then deposited 402 ontop of the first segment, first warp group. The first segment, secondwarp group is then deposited 404 on top of the first weft filament andnext to the first segment, first warp group. In most embodiments, thefirst segment, second warp group deposits are at least twice as long asthe first segment, first warp group deposits. The second weft filamentis then deposited 406 on top of the first segment, second warp group.This is followed by the second segment, first warp group 408 over thesecond weft filament. This is followed by the third weft filament 410 ontop of the second segment, first warp group. The second segment, secondwarp group is then deposited 412 over the third weft filament, and theprocess repeats 414 until the entire first layer of the part is made.When the entire first layer of the part is complete, the warp filamentsare cut and fabrication of the next layer of the part begins the sameway. Persons having ordinary skill in the art will understand that asimilar process will be used to deposit other types of plain-weavecomposites. Examples include, but are not limited to, plain-weavecomposites having more than one warp filament interlaced with the weft(e.g. “duck” weave having two warp filaments interlaced with one weftfilament), or vice-versa.

More complicated weaving patterns may require more than two groups ofwarp filaments. For a particular weaving pattern, the minimum number ofwarp groups is equal to the maximum number of warp filaments the weftwill pass over plus the maximum number of warp filaments the weft willpass under. For example, FIG. 5 illustrates the deposition sequence fora 2/2 twill weave. The process begins with the first segment, first warpgroup and first segment, second warp group being deposited together 500,followed by the first weft filament 502. This is followed by the firstsegment, third warp group and first segment, fourth warp group beingdeposited together 504. Then the second segment, first warp group andsecond segment, fourth warp group are deposited together 506, followedby the second weft filament 508. Then the second segment, second warpgroup and second segment, third warp group are deposited together 510.This is followed by the third segment, third warp group and thirdsegment, fourth warp group being deposited together 512, followed by thethird weft filament 514. Then the third segment, first warp group andthird segment, second warp group are deposited together 516, followed bythe fourth segment, second warp group and fourth segment, third warpgroup 518. The fourth weft filament is then deposited 520, followed bythe fourth segment, first warp group and fourth segment, fourth warpgroup 522. This completes the pattern for a 2/2 twill, which thenrepeats. Persons having ordinary skill in the art will understand that asimilar process will be used to deposit other types of twill-weavecomposites. Examples include, but are not limited to, 1/2, 1/3, 2/1,3/1, and 3/3 twill-weave composites.

FIG. 6 illustrates the deposition sequence for a 1/4 satin-weavecomposite. At 600, the first segment, first warp group is deposited. At602, the first weft filament is deposited. At 604, the first segments,second, third, fourth, and fifth warp groups are deposited. At 606, thesecond segment, second warp group is deposited. At 608, the second weftfilament is deposited. At 610, the second segments, first, third,fourth, and fifth warp groups are deposited. At 612, the third segment,third warp group is deposited. At 614, the third weft filament isdeposited. At 616, the third segments, first, second, fourth, and fifthwarp groups are deposited. At 618, the fourth segment, fourth warp groupis deposited. At 620, the fourth weft filament is deposited. At 622, thefourth segments, first second, third, and fifth warp groups aredeposited. At 624, the fifth segment, fifth warp group is deposited. At626, the fifth weft filament is deposited. At 628, the fifth segments,first, second, third, and fourth warp groups are deposited. Personshaving ordinary skill in the art will understand that a similar processwill be used to deposit other types of satin-weave composites. Examplesinclude, but are not limited to, 1/5, 1/6, 4/1, 5/1, etc. satin-weavecomposites

In some embodiments, the deposition sequence can also be tailored toproduce different weaving patterns at different locations within thesame plane of a single interlaced composite structure. Neitherhand-layup FRP nor automated tape-placement machines can achieve thiseffect. FIG. 7 illustrates a composite which integrates three differentweaves within the same interlaced structure to provide differentmaterial properties in different locations. The weave in FIG. 7transitions from a plain weave 700 to a twill weave 702 to a satin weave704. As the weave within the layer transitions from plain weave 700 tosatin weave 704, the shear strength will decrease and the in-planestrength will increase. The same is true for stiffness and impactresistance.

In some embodiments, multiple layers can be deposited at the same time.In these embodiments, a first two more groups of warp filaments and aweft filament are deposited in the manner described above. However,before advancing to the next weft filament in that layer, a second twoor more additional groups of warp are deposited on top of the layer,along with another weft filament, creating two layers of interlacedcomposite. The number of layers which can be deposited at once is onlylimited by the sophistication of the deposition machine and the numberof warp groups available. In some embodiments, this technique can alsointerlace warp filaments between layers. Using the two-layer exampledescribed above, the warp groups would alternate between which layer wasdeposited first for each weft location. Thus, after the first weftlocation, at the next weft location the second two or more warp groupsand their weft filament deposit first, followed by the first two or morewarp groups and their weft filament. In this way, the first two or morewarp groups are now in the upper layer and the second two or more warpgroups are in the lower layer.

In most embodiments, the warp and weft are orthogonal to each other.However, in some embodiments, favorable material properties may beachieved by creating a smaller angle (less than 90°) between the warpand weft. For example, FIG. 8 illustrates a plain weave where the warpand weft are at a 45° to each other.

In some embodiments, the gaps between filaments may be filled in withadditional resin as a post-processing operation. In other embodiments,the filaments may be spaced closely enough together to fuse togetherduring deposition to create a void-free layer. In further embodiments,the filaments may be spaced closely enough together during depositionthat a post-processing step can eliminate any gaps. For example, thefinal part may be removed, heated, and compressed to re-flow the matrixof the filaments, causing it to fill in the gaps and expel any gassestrapped in the gaps.

However, in some embodiments, the gaps may be intentionally left inplace to reduce density and crack propagation. For example, in somecombinations of resin and fiber, filling the gaps may reduce thestrength and/or impact resistance of the final composite part becausefilling the gaps with resin promotes crack propagation. In someembodiments, the strength and impact resistance of the final part may beespecially sensitive to cracks near the interface between the resin andthe reinforcing fiber. In these embodiments, leaving the gaps empty mayeliminate a pathway for cracks to propagate to this interface, resultingin superior mechanical properties. In other embodiments, leaving thegaps empty may improve the buckling resistance of the filaments andcorrespondingly improve the overall compressive strength of the part. Inthese embodiments, the high interfacial strength resulting from allowthe gaps to remain allows the fibers to act as reinforced columns ofresin where the reinforcing fiber acts as “rebar.”

Filament Design

In an exemplary embodiment, the filament includes a high-performancereinforcing yarn coated with a polymer resin to create a compositefilament. In some embodiments, the polymer is an engineering polymer. Inan exemplary embodiment, the resin is polyetherketoneketone (PEKK).

Several mechanical and processing parameters are relevant to theprocessing behavior and final mechanical properties of the composite,including melt viscosity, melt temperature, stiffness, toughness,density, and chemical and thermal stability. Because the reinforcingfibers provide most of the strength and stiffness in the resultingcomposite, an appropriate fiber should be selected for the compositefilament to achieve optimal performance. In some embodiments, theinterface between resin and the reinforcing fiber has the strongestinfluence on the composite's properties. If the interface is weak, thefiber will pull out of the matrix and fail to carry load, resulting in alower overall composite strength. Therefore, in some embodiments,surface modification (e.g. etching, sizing) of the fiber may be requiredfor the filament to exhibit good interfacial strength. In someembodiments, nylon 6 or nylon 6,6 may be paired with unsized carbonfiber. In an exemplary embodiment, PEKK resin may be paired with unsizedcarbon fiber.

In some other embodiments, the reinforcing fibers may be aramid (e.g.Nomex®, Kevlar®), metals, glass, silicon carbide, zirconium oxide, oraluminum oxide. Persons skilled in the art will understand that othersuitable reinforcing fibers may also be used. In some embodiments,different warp filaments with different reinforcing fibers and/or resinsmay deposited. In some embodiments, all the warp filaments in a warpgroup may be same. In other embodiments, the warp filaments in a warpgroup may be different.

In some other embodiments, the filament may include a thermoset resin.In these embodiments, the thermoset resin is uncured during deposition.The resin is cured after deposition, resulting in bonding between thewarp and weft filaments. In some embodiments, the resin may beselectively cured during each step in the deposition sequence. In someother embodiments, the resin of an entire layer may be curedsimultaneously. In some embodiments, the resin may be cured by UV light.In some other embodiments, the resin may be cured by applying heat. Inthese embodiments, the heat may be applied by conduction, convection,radiation, or any combination of the three.

In some embodiments, the filaments may include comingled thermoplasticresin fibers and reinforcing fibers instead of reinforcing fiberspre-impregnated or pre-coated with resin. In these embodiments, theresin is melted during the deposition process and wets the reinforcingfibers at that time.

In some embodiments, the filament used may be a single-polymerthermoplastic fiber or yarn of multiple thermoplastic fibers. In theseembodiments, the resin is not melted during deposition. Instead, thewarp and weft are melted and fused where they interlace afterdeposition. This may occur locally (for example by laser or heatedroller) or an entire layer may be fused by passing a heat source overit. This process may be desired if a lightweight component is desiredwith lower stiffness than would be produced by a reinforced composite.

Warp Deposition

The mechanical system of the composite printer can be considered acombination of a jacquard loom and an FDM printer. Referring now to FIG.9, which illustrates a simplified version of the composite printer 900,the base unit of the printer is the warp print head 902 (warp head),which deposits the warp filaments on a print plate 916. Multiple warpheads may be incorporated into a warp rack 920. A weft inserter (notshown) allow the weft to be woven into the warp filaments extruded fromeach warp head 902. As described above, the warp heads 902 in the warprack 920 move relative to each other between weft insertions to controlthe weave geometry.

In one embodiment, the warp heads 902 are each supported by a guide rod906 and a lead screw 904. The lead screw 904 also drives the motion ofthe warp heads 902. The lead screws 904 and guide rods 906 are supportedby end plates 908. The end plates 908 and the print plate 916 aresupported by a frame 910. Each lead screw 904 is driven by a motor 918.In some embodiments, the lead screws 904 and guide rods 906 may bealternated from the top to bottom position in alternating warp heads 902to accommodate more tightly packed warp heads 902. In anotherembodiment, additional mounted plates 908 may be provided farther backfrom the printing space to accommodate additional motors 918 connectedto longer lead screws 904. These embodiments also allow higher warp-headdensities. In some embodiments, the lead screw 904 may be connected tothe motor 918 through a flexible coupling 912. In some embodiments, thenon-driven end of the lead screw 904 may be supported by a floatingbearing to prevent binding. In some embodiments, motor and/or lead screwmay be fitted with an encoder to indicate the position of the warp head902 to a control device. In some embodiments, the motors may be steppermotors. In some other embodiments, the motors may be servo motors,direct-current motors, or alternating-current motors, as may beunderstood by one having ordinary skill in the art.

In some other embodiments, the warp heads 902 may be supported by one ormore beams or by multiple guide rods, as may be understood by one havingordinary skill in the art. In further embodiments, the warp heads 902may be driven by linear motors, chains, belts, pneumatics, orhydraulics, as may be understood by one having ordinary skill in theart.

FIGS. 10 and 11 respectively illustrate one embodiment of a warp head902 and a cross-section of that warp head 902. The warp head 902includes a motive section 930, a heater section 932, and a cover plate934. In this embodiment, a combination of lead screws, bearings, andguide rods drives the warp head 902 through the motive section 930. Inthe simplest configuration, the motive section 930 includes two throughholes 936 for the guide rod 906 and the lead screw 904, respectively.Two transverse holes 938 allow mounting of a ball screw for the leadscrew 904 or a linear bearing for the guide rod 906. As the motor 918turns, the lead screw 904 transfers the rotational motion into linearmotion, while the guide rod 906 serves to prevent the warp head 902 fromrotating. Self-aligning bearings are used to prevent the warp head 902from binding with the guide rod.

In one embodiment, the composite filament enters the warp head in thesolid state, where it is heated and extruded. The heater section 932mates to the cover plate 934. The heater section includes a cavity for aheating element 940. In one embodiment, the heating element may be aceramic cartridge heater. In other embodiments, the heating element mayanother resistive element, such as nichrome wire, or an inductive coil,as will be understood by one having ordinary skill in the art. Thefilament to be deposited travels through a channel 942 between theheater section 932 and the cover plate 934. In some embodiment, the warphead 902 may not have a heater section 932. In some of theseembodiments, the thermoplastic resin of the filament may be meltedremotely as it is deposited, for example by a laser.

The warp filament is preferably supplied from a reel (not shown). Thereel is preferably stationary, and mounted remotely from the warp head902. The filament should be kept under tension to control its placement.In one embodiment, a roller (not shown) on the warp head appliespressure against the print plate 916 to create tension on the filamentduring deposition. The tension pulls the filament off a tensioned reel(not shown). This may be described as a “filament pulling” system. Inanother embodiment, the “filament pushing” system, pair of poweredrollers (not shown) pulls the filament off the reel and forces it intotube (not shown) which guides the filament to the warp head 902. Thisembodiment is like the drive system of a MIG welder for delivering thewelding wire to the torch, as will be understood by one having ordinaryskill in the art. The overall force on the filament during the extrusionprocess is a combination of tension on the filament embedded in themolten filament and pressure in the warp head. In another embodiment,tension in the filament can be controlled by varying the torque on thelead screw 904.

FIGS. 12 and 13 illustrate two views of a more sophisticated printer1200. More complex 3D composite structures can be achieved by addingadditional warp racks to the printer 1200. In this embodiment, there isa primary warp rack 1210 and a secondary warp rack 1220. The primarywarp rack 1210 operates as described above. The warp heads 1222 on thesecondary warp rack 1220 have their own guide rods 1224 and lead screws1226, positioned above the guide rods 1214 and lead screws 1216 for theprimary warp rack 1210. The guide rods 1214 and lead screws 1216 for theprimary warp rack 1210 pass through the lower portion of the secondarywarp heads 1222 on bearings that allow the secondary warp heads 1222 tomove independently of the primary warp heads 1212. The heating element1228 and extruder 1230 of the secondary warp heads are position at thesame height as the heating element 1218 and extruder 1208 of thesecondary warp heads. As described above, additional warp racks allowdeposition of multiple layers of composite in a single pass. They alsoallow interlacing between layers, as described above.

Print Plate

The print plate 916, 1270 is a component of the printer system. In oneembodiment, the print plate 916 moves solely in the vertical (“Z”) axis.As each layer of composite is completed, the print plate 916 drops downso that a new layer can be deposited on top of the previous later.

A more sophisticated print plate 1270 is shown in FIGS. 12 and 13. Inaddition to moving in the Z axis, the print plate 1270 for this printerrotates about the Z-axis. This allows the fiber orientation to bechanged between layers, which can provide beneficial material propertiesin the final composite part. In one embodiment, rotation about the Zaxis is achieved by a planetary gear configuration on the underside ofthe print plate. In this embodiment, the planet carriers are fixed sothat rotation of the sun gear results in rotation of the ring gear, aswill be understood by those skilled in the art. As described above, theprint plate 1270 also descends as layers are printed, which maintains aconstant gap between the warp heads 1212, 1222 and the print plate 1270.The vertical motion may be achieved using lead screws, hydraulic orpneumatic lifts, linear actuators, or other means as will be understoodby one having ordinary skill in the art.

In some embodiments, the print plate 1270 also moves in a directiontransverse to the motion of the warp heads. This transverse motionallows deposition of warp filaments which is closer together than thecenter-to-center distance between the warp heads. For example, in oneembodiment, after a layer is completed, the print plate 1270 can movetransversely by an amount equal to one-half the pitch between the warpheads and repeat the layer. This technique results in a higher warpdensity than repeating the warp filaments on top of one another, becausethe second-layer warp filaments will “settle” in the spaces between thefirst-layer warp filaments.

In some embodiments, the print plate 1270 also rotates about axesorthogonal to the Z axis. In these embodiments, the print plate cantilt, allowing the creation of more complicated three-dimensionalcomposite structures. In an exemplary embodiment, the print plate canmove linearly in three orthogonal directions and rotate about three axesparallel to those directions.

In some embodiments, the print plate 1270 will be heated during theprinting process. This controls the cooling rate of the thermoplasticresins. In one embodiment, the print plate 1270 may be heated by aresistive heating element embedded into the print plate. Unlike the warpheads 1212, 1222, which require an operating temperature above the melttemperature of the thermoplastic matrix, the print plate 1270 operatesbelow the melt temperature and therefore requires less precisetemperature control than the warp heads. In other embodiments, the printplate may be heated by a heated fluid, such as water or a water-glycolmixture, or by steam. As will be understood by one skilled in the art,many methods for controlling the temperature of thermoplastic molds maybe used to control the temperature of the print plate 1270.

In some embodiments, the print plate 1270 may be treated with apermanent surface treatment, such polytetrafluoroethylene (PTFE), topromote releasing the final composite part. In other embodiments, theprint plate 1270 may be treated before each part with a temporaryrelease agent, for example a silicone fluid, as will be understood byone having ordinary skill in the art.

Compression Roller

In some embodiments, the printer may include a compression roller 1260.In these embodiments, the compression roller 1260 compresses theinterlaced composite structure between deposition of layers. In someembodiments this provides greater consistency in the final compositepart. In other embodiments, the compression roller 1260 may be heated.The heating may serve one or more purposes: (1) controlling the coolingof the molten thermoplastic resin in the filaments; (2) melting, orre-melting, the thermoplastic resin to ensure a high-quality bondbetween the composite filaments (including without limitationwarp-to-weft bond and layer-to-layer bond); and (3) curing thermosetresins in composites that employ them.

In one embodiment, the compression roller 1260 has a pair of motivesections 1264 which are driven by at least two lead screws 1266 and twoor more guide rods 1268. The lead screws 1266 drive the motive sections1264 which in turn carry the compression roller 1260 with them. Incertain embodiments, the compression roller 1260 may incorporate one ormore drive motors 1262. In some embodiments, the drive motor(s) 1262 mayprovide all the motive power and the motive sections may run on fourguide rods 1268. In other embodiments, the drive motor(s) 1262 work inconcert with the lead screws 1266 to move the compression roller 1260 s.

Weft Insertion

The weft inserter should be able to start and end each insertioncompletely outside of the print space, to allow the warp heads to movebetween insertions. FIGS. 12 and 13 also illustrate one embodiment of aweft insertion system 1240. In this embodiment, the weft is inserted bya rack-and-pinion rapier 1242. In one embodiment, the rapier 1242includes a rack 1244 (a series of linear gear teeth) which is driven bya matching geared pinion 1246, as will be understood by one skilled inthe art. In another embodiment, the rack 1244 may be a smooth-walledtrack driven by a smooth rubber wheel as the pinion 1246. The pinion1246 is driven by a motor 1248. As the pinion 1246 turnscounterclockwise, the rapier 1242 extends into the print space 1244,carrying the weft filament with it. In this embodiment, the rack 1244and rapier 1242 are stiff. In one embodiment, the weft filament is drawnfrom a tensioned spool (not shown) by the insertion motion. In anexemplary embodiment, the pinion 1246 then reverses and turns clockwiseto withdraw the rapier 1242, depositing the weft as the rapier 1242 iswithdrawn. The weft is then cut (see below for cutting techniques) nearthe pinion 1246. In another embodiment, the weft is deposited during theinsertion of the rapier 1242 and the weft is cut after being inserted tothe proper distance. The pinion 1246 then reverses and turns clockwiseto withdraw the rapier 1242.

In one embodiment, the weft is not melted during insertion, because themolten warp filaments will bond to the weft when they are deposited. Inanother embodiment, a heating module (not shown) may be added to the endof the rapier to deposit molten weft filament. In another embodiment,the rapier 1242 may be a flexible metal tape driven by a sprocket ordrive roller, as will be understood by those skilled in the art.

In this embodiment the entire weft insertion system 1240 travels thelength of the print space in the same direction as the warp heads 1204,1296. This allows insertion of the weft at the proper location. In oneembodiment, the weft insertion system 1240 rides on two guide rails 1248and is driven by a lead screw 1250 and motor 1252. In other embodiments,the weft insertion system may be driven by linear motors, chains, belts,pneumatics, or hydraulics, as may be understood by one having ordinaryskill in the art.

FIG. 14 illustrates another embodiment of a weft insertion system. Inthis embodiment, the air jet insertion system 1400, a pulse ofcompressed air ejects a pre-cut weft filament to inset it between warpfilaments. The air jet insertion system 1400 should travel the length ofthe print space in the same direction as the warp heads 1204, 1296, aswith the rapier insertion system. In this embodiment, the systemincludes a nozzle 1402, a compressed air reservoir 1404, a primary airvalve 1406, a weft cutter 1408, a weft reel 1410, and a weft extruder1412. During operations, the weft extruder 1412 draws weft filament fromthe weft reel 1410 and feeds it into the nozzle 1402 to the desiredlength. The weft cutter 1408 cuts the weft filament, for example by ablade through a cutter slot 1414. The weft extruder 1412 includes an airvalve to prevent compressed air entered the weft reel 1410 housing. Theweft extruder 1412 valve then closes and the primary air valve 1406 thenopens for a controlled period, applying pressure the cut weft filamentand expelling it from the nozzle 1402. Because the filament ispre-impregnated with resin, it retains sufficient stiffness to remainstraight as it is ejected from the nozzle 1402. In an exemplaryembodiment, the ejected weft filament stops when it strikes a stop plate(not shown) on the opposite side of the printing area. In oneembodiment, the print plate is fixed. In another embodiment, the printplate can mover transversely to the warp heads to alter the finalresting place of the ejected weft filament. As with the rapier weftinsertion systems, the air jet weft insertions system 1400 should travelthe length of the print space in the same direction as the warp heads toinsert the weft in the same location. All the mechanisms discussed abovefor such motion are appropriate for the air jet weft inserter as well.

Filament Cutting

As noted above, the deposited warp and weft filaments should be cut oncethey reach the desired length. Several methods may be used to cut thefilaments. In one embodiment, an extendable scissors may be used. FIG.15 illustrates the cutting mechanism of one embodiment of the extendablescissors. In one embodiment, the cutting mechanism extends into theprinting space on a rapier, like that used for the weft inserter. Aswith the weft inserter, the extendable scissor mechanism may be drivenby a rack and pinion, linear motors, chains, belts, pneumatics, orhydraulics, as may be understood by one having ordinary skill in theart. The extendable scissors allow filaments to be cut independently,which enables more complicated shapes to be printed. For cutting warpfilaments, the extendable scissors are mounted at the end of the printerand the rapier extends in the direction of warp motion to cut thefilaments. In some embodiments, a single extendable scissor cutter maytraverse across all the warp heads, cutting each warp filamentindividually. This simplifies control of the cutting and enablesselective cutting of filaments, for example to create holes forfasteners without damaging the integrity of the composite. In anotherembodiment, each warp head may have its own extendable scissors. Thisembodiment provides higher operating speed for the machine. In anotherembodiment, a cutting system (such as the scissors) may be integratedinto the warp heads to increase operating speed.

The cutting mechanism includes two cutting blades 1502, two levers 1504;a primary pivot 1506, two secondary pivots 1508, a frame 1510, and ahollow rapier 1512. The levers 1504 are connected to the cutting blades1502 on one end at the secondary pivots 1508. The other ends of thelevers 1504 are free. The cutting blades are rotatably fixed to theframe 1510 at the primary pivot 1506. During cutting operation, a wireor rod (not shown) within the hollow rapier 1512 pulls on the free endsof the levers 1504, drawing them away from primary pivot. The pullingforce tends to pull the secondary pivots 1508 and the ends of thecutting blades 1502 toward the hollow rapier 1512. This imparts a momenton the cutting blades 1502 which rotate about the primary pivot 1506,causing a cutting action.

In another embodiment, a rotary cutter may be used to cut the filaments.FIG. 16 illustrates one embodiment of a roller cutter. The roller cutterincludes a rotary blade 1602, a pivot 1606, and a housing 1608. Therotary blade has a sharpened, ground edge 1604. The rotary cutter ismounted on the end of an extendable arm. Unlike the rapier used for theweft insertion or the extendable scissors, the arm for the rotary cuttershould be fairly robust because it should be stiff enough to providedown force for cutting.

In operation, the arm extends into the printing space transversely tothe filaments to be cut. For example, to cut warp filaments, the rotarycutter extends into the cutting space in a direction transverse to themotion of the warp heads. The arm provides a down force between theprinting plate 916, 1270 and the rotary blade 1602. As the rotary blade1602 passes over each filament, the filament is severed between therotary blade 1602 and the printing plate 916, 1270. Although thedistance to which the rotary cutter is extends is controlled, it willcut all the filaments it passes over. Therefore, composite structureswith complicated edge geometries should be carefully positioned withinthe cutting space so that the rotary cutter can cut all the filamentsneeded, without cutting unwanted filaments. This limitation means thatthe rotary cutter is unsuitable for composite structures to be printedwith holes in their interiors.

In another embodiment, a drag knife style cutter may be used to cut thefilaments. FIG. 17 illustrates one embodiment of a drag knife cutter.The drag knife includes a blade 1702 with a cutting point 1704, a frame1706, a blade chuck 1708. The blade chuck 1708 holds the blade 1702securely against the frame 1706. The blade chuck 1708 is held by a screw1710. In one embodiment, the blade 1702 may be a standard utility-knifeblade. In another embodiment, the blade may be a sharpened cutter madefrom high speed steel, tungsten carbide, diamond, sapphire, or anothersuitably hard material. A person having ordinary skill in the art willunderstand that other blade materials may also be appropriate, dependingon the filament materials. The drag knife cutter is mounted to anextendable arm, like the rotary cutter. Like the rotary cutter, theextendable arm should be stiff enough to provide the necessary downforce for cutting.

In operation, the arm extends into the printing space transversely tothe filaments to be cut. For example, to cut warp filaments, the dragknife cutter extends into the cutting space in a direction transverse tothe motion of the warp heads. The arm provides a down force between theprinting plate 916, 1270 and the drag knife 1602. As the drag knife 1602passes over each filament, the filament is severed between the dragknife 1602 and the printing plate 916, 1270. In one embodiment, the dragknife is fixed to the end of the arm, and has the same limitations asthe rotary cutter. In another embodiment, an auxiliary actuator can liftthe drag knife slightly from the cutting surface, allowing selectivecutting of filaments as the drag knife passes across the print plate.

The design and functionality described in this application is intendedto be exemplary in nature and is not intended to limit the instantdisclosure in any way. Those having ordinary skill in the art willappreciate that the teachings of the disclosure may be implemented in avariety of suitable forms, including those forms disclosed herein andadditional forms known to those having ordinary skill in the art. Forexample, one skilled in the art will recognize that executableinstructions may be stored on a non-transient, computer-readable storagemedium, such that when executed by one or more processors, causes theone or more processors to implement the method described above.

While certain embodiments of this disclosure have been described inconnection with what is presently considered to be the most practicaland various embodiments, it is to be understood that this disclosure isnot to be limited to the disclosed embodiments, but on the contrary, isintended to cover various modifications and equivalent arrangementsincluded within the scope of the appended claims. Although specificterms are employed herein, they are used in a generic and descriptivesense only and not for purposes of limitation.

This written description uses examples to disclose certain embodimentsof the technology and to enable any person skilled in the art topractice certain embodiments of this technology, including making andusing any apparatuses or systems and performing any incorporatedmethods. The patentable scope of certain embodiments of the technologyis defined in the claims, and may include other examples that occur tothose skilled in the art. Such other examples are intended to be withinthe scope of the claims if they have structural elements that do notdiffer from the literal language of the claims, or if they includeequivalent structural elements with insubstantial differences from theliteral language of the claims.

What is claimed is:
 1. A machine for fabricating three-dimensionalinterlaced composite components comprising: a frame; a depositionsurface; a first set of two or more warp heads adapted to: deposit afirst set of warp filaments on the deposition surface in a first warpdirection; and move parallel to one another within a first plane; asecond set of two or more of warp heads adapted to: deposit a second setof warp filaments on the deposition surface in a second warp direction;and move parallel to one another within the first plane; wherein thesecond set of warp heads do not move collinearly with the first set ofwarp heads; and a weft inserter adapted to: deposit a set of weftfilaments on the deposition surface in a weft direction; and traverse alength of the deposition surface in the warp direction; wherein the weftdirection is different than at least one of the first and second warpdirections.
 2. The machine of claim 1, wherein the first set warp heads,the second set warp heads, and the weft inserter are each supported bythe frame.
 3. The machine of claim 1, wherein the deposition surface issupported by the frame.
 4. The machine of claim 1, wherein the firstwarp direction is the same as the second warp direction.
 5. The machineof claim 1, wherein the first warp direction is different than thesecond warp direction.
 6. The machine of claim 1, wherein the weftdirection is different than both the first and second warp directions.7. The machine of claim 1, wherein the weft inserter comprises a rapierweft inserter comprising a linear element that extends over thedeposition surface.
 8. The machine of claim 1, wherein the weft insertercomprises an air-jet weft inserter comprising: a compressed air supply;at least one compressed air control valve; a filament cutter; and anozzle.
 9. The machine of claim 1 further comprising a filament cutter.10. The machine of claim 1, wherein the deposition surface is adapted tomove linearly in a vertical direction along a vertical axis.
 11. Themachine of claim 1, wherein the deposition surface is adapted to rotatein a plane normal a vertical axis.
 12. The machine of claim 1, whereinthe deposition surface is adapted to: move linearly in a verticaldirection along a vertical axis; and rotate in a plane normal thevertical axis.
 13. The machine of claim 1 further comprising: a thirdset of two or more warp heads adapted to: deposit warp filaments on thedeposition surface in a third warp direction; and move parallel to oneanother and collinearly with the first set of warp heads; and a fourthset of two or more warp heads adapted to: deposit warp filaments on thedeposition surface in a fourth warp direction; and move parallel to oneanother collinearly with the second set of warp heads.
 14. The machineof claim 1 fabricating a three-dimensional interlaced composite by:depositing onto the deposition surface the first set warp filaments;inserting, on top of the first set of warp filaments, a first set ofweft filaments; depositing, on top of the first set of weft filaments,the second set of warp filaments; and inserting, on top of the secondset of warp filaments, a second set of weft filaments; wherein thethree-dimensional interlaced composite is formed when at least one ofthe warp filaments passes over at least one of the weft filaments andpasses under at least another of the weft filaments.
 15. Athree-dimensional interlaced composite fabricated by the machine ofclaim 14 comprising: the first set warp filaments; and the first setweft filaments.
 16. An interlaced composite component comprising: afirst set of two or more warp filaments parallel to each other; and afirst set of two or more weft filaments parallel to each other; whereinat least a portion of the warp filaments of the first set of warpfilaments are interlaced with, and bonded to, at least a portion of theweft filaments of the first set of weft filaments; wherein at least aportion of the warp filaments and at least a portion of the weftfilaments are interlaced in at least two different weave patternsselected from the group consisting of plain weave, twill weave, andsatin weave; and wherein at least a portion of the warp filaments and atleast a portion of the weft filaments are continuous and the weavepatterns transition from one pattern to another.
 17. The interlacedcomposite component of claim 16, wherein at least a portion of the warpfilaments comprise reinforcing fibers bonded to a polymer matrix. 18.The interlaced composite component of claim 16, wherein at least aportion of the warp filaments comprise reinforcing fiberspre-impregnated with thermoplastic resin.
 19. The interlaced compositecomponent of claim 16, wherein at least a portion of the warp filamentsand at least a portion of the weft filaments comprise comingledreinforcing fibers and thermoplastic fibers.
 20. The interlacedcomposite component of claim 16 further comprising: a second set of twoor more warp filaments parallel to each other; and a second set of twoor more weft filaments parallel to each other; wherein at least aportion of the weft filaments of the first set of weft filaments areparallel to one other and substantially coplanar; wherein at least aportion of the weft filaments of the second set weft filaments areparallel to one other, substantially coplanar, and positioned eitherabove or below at least a portion of the first set of weft filaments;wherein at least a portion of the warp filaments of the first set ofwarp filaments alternate between being interlaced with, and bonded to,at least a portion of the weft filaments of the first set of weftfilaments and at least a portion of the weft filaments of the second setof weft filaments; and wherein at least a portion of the warp filamentsof the second set of warp filaments alternate between being interlacedwith, and bonded to, at least a portion of the weft filaments of thefirst set of weft filaments and at least a portion of the weft filamentsof the second set of weft filaments.
 21. The interlaced compositecomponent of claim 20, wherein: wherein at least a portion of the warpfilaments of the second set of warp filaments and at least a portion ofthe weft filaments of the second set of weft filaments are interlaced inat least two different weave patterns selected from the group consistingof plain weave, twill weave, and satin weave; and wherein at least aportion of the warp filaments of the second set of warp filaments and atleast a portion of the weft filaments of the second set of weftfilaments are continuous and the weave patterns transition from onepattern to another.
 22. An interlaced composite component comprising: afirst set of two or more warp filaments parallel to each other; and afirst set of two or more weft filaments parallel to each other; whereinat least a portion of the warp filaments of the first set of warpfilaments are interlaced with, and bonded to, at least a portion of theweft filaments of the first set of weft filaments; wherein at least aportion of adjacent warp filaments of the first set of warp filamentsare separated from one another by a warp gap; wherein at least a portionof adjacent weft filaments of the first set of weft filaments areseparated from one another by a weft gap; and wherein the warp and weftgaps define one or more openings in the composite component.
 23. Theinterlaced composite component of claim 22 further comprising athermoplastic polymer; wherein the thermoplastic polymer is molded overthe interlaced composite component.
 24. The interlaced compositecomponent of claim 23, wherein the thermoplastic polymer is reinforcedwith a discontinuous fiber.